Epoxy Resin WOC-87-II(A)/113-1(B)
Contact Info
- Add:1 Chuangzhi Road,Jianye District, Zip:
- Contact: Fang
- Tel:86-25-8526 2519
- Email:sales@crossinchem.com
Other Products
■ Description
Two-component encapsulating system based on epoxy resin,formed from auxiliaries including epoxy resin, diluent, compound amine, cross-linking agent and defoamer by special production processing
Excellent of the surface gloss of the cured epoxy resin, High/Low temperature resistance is good, excellent electrical properties and have flame retardant property.
■ Applications
Encapsulation of electrical components of Capacitor, Igniter, Transformer, trigger and Filter.
■ General properties
|
Test Item |
Test Mothed/Conditions |
WOC-87-II A |
113-1 B |
|
Appearance |
Visualization |
Black viscous liquid |
Dark brown liquid |
|
Density |
25º C g/m³ |
1.58 – 1.70 |
1.0 – 1.15 |
|
Viscosity |
40º C mpa.s |
1000 - 5000 |
20 - 80 |
|
Viscosity(blended) |
40º C mpa.s |
500 |
|
|
Storage validity |
Sealed and storage Temp.below 25º C |
6 months |
6 months |
|
Ratio of blend |
Weight/Weight |
100 |
20-25 |
|
Curing condition |
º C/hrs |
25 º C/24h |
|
■ Characteristics after curing
|
Item |
Unit/Conditions |
WOC-87-II A/113-1 B |
|
Hardness |
20º C Shore-D |
≥70 |
|
Insulation Strength |
25º C kv/mm |
≥18 |
|
Bending Strength |
Kg/cm2 |
≥82 |
|
High Temperature Resistance |
150º C |
Not cracking after 5 hours |
|
Flame Retardancy |
UL 94 |
V0 or V1 |
|
Surface Resistance |
25º C Ω.cm |
＞1014 |
|
Volume Resistance |
25º C Ω.cm |
＞1015 |
|
Curing Shrinkage Rate |
% |
＜0.6 |